SteelAISIChromium Vanadium Steel (Alloy 61XX)
Chromium Vanadium Steel (Alloy 61XX) Steel Properties
The below table outlines the material properties for Chromium Vanadium Steel (Alloy 61XX) material including the young's modulus, yield strength, ultimate strength and other relevant mechanical properties required for structural and mechanical design.
Chromium Vanadium Steel (Alloy 61XX) Young's Modulus
The Young's Modulus of Chromium Vanadium Steel (Alloy 61XX) is 29,700 ksi.
Chromium Vanadium Steel (Alloy 61XX) Ultimate Strength
The Ultimate Strength of Chromium Vanadium Steel (Alloy 61XX) ranges between 69 and 180 ksi.
Chromium Vanadium Steel (Alloy 61XX) Yield Strength
The Yield Strength of Chromium Vanadium Steel (Alloy 61XX) ranges between 42 and 178 ksi depending on the material grade. See the below tables to get your specific material grade material strength.
Alloy 6118 Steel Properties
General Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 205,000 MPa | 7,850 kg/m3 | 470 MPa | 290 MPa | 13 1/°C | 0.29 |
| Imperial | 29,700 ksi | 491 lb/ft3 | 69 ksi | 42 ksi | 7.22 1/°F | 0.29 |
Alloy 6150 Steel Properties
Annealed Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 205,000 MPa | 7,850 kg/m3 | 670 MPa | 415 MPa | 12 1/°C | 0.29 |
| Imperial | 29,700 ksi | 491 lb/ft3 | 97 ksi | 60 ksi | 6.62 1/°F | 0.29 |
Normalized Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 205,000 MPa | 7,850 kg/m3 | 972 MPa | 640 MPa | 13 1/°C | 0.29 |
| Imperial | 29,700 ksi | 491 lb/ft3 | 141 ksi | 93 ksi | 7.22 1/°F | 0.29 |
Oil quenched Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 205,000 MPa | 7,850 kg/m3 | 1,240 MPa | 1,225 MPa | 12 1/°C | 0.29 |
| Imperial | 29,700 ksi | 491 lb/ft3 | 180 ksi | 178 ksi | 6.62 1/°F | 0.29 |
Alloy 6150H Steel Properties
Annealed Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 205,000 MPa | 7,850 kg/m3 | 670 MPa | 415 MPa | 12 1/°C | 0.29 |
| Imperial | 29,700 ksi | 491 lb/ft3 | 97 ksi | 60 ksi | 6.62 1/°F | 0.29 |
Normalized Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 205,000 MPa | 7,850 kg/m3 | 972 MPa | 640 MPa | 13 1/°C | 0.29 |
| Imperial | 29,700 ksi | 491 lb/ft3 | 141 ksi | 93 ksi | 7.22 1/°F | 0.29 |
Oil quenched Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 205,000 MPa | 7,850 kg/m3 | 1,240 MPa | 1,225 MPa | 12 1/°C | 0.29 |
| Imperial | 29,700 ksi | 491 lb/ft3 | 180 ksi | 178 ksi | 6.62 1/°F | 0.29 |