ASTM A743 Steel Properties

The below table outlines the material properties for ASTM A743 material including the young's modulus, yield strength, ultimate strength and other relevant mechanical properties required for structural and mechanical design.

Cast Stainless Steel

CA15
CA15M
CA40
CA6NM
CF3
CF3M
CF3MN
CF8
CF8C
CF8M
CH10
CF16F
CH20
CK20

ASTM A743 Young's Modulus

The Young's Modulus of ASTM A743 is 200,000 MPa.

ASTM A743 Ultimate Strength

The Ultimate Strength of ASTM A743 ranges between 450 and 755 MPa.

ASTM A743 Yield Strength

The Yield Strength of ASTM A743 ranges between 195 and 550 MPa depending on the material grade. See the below tables to get your specific material grade material strength.

Cast Stainless Steel Steel Properties

CA15 Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	620 MPa	450 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	90 ksi	65 ksi	6.67 1/°F	0.29

CA15M Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	620 MPa	450 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	90 ksi	65 ksi	6.67 1/°F	0.29

CA40 Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	690 MPa	485 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	100 ksi	70 ksi	6.67 1/°F	0.29

CA6NM Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	755 MPa	550 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	110 ksi	80 ksi	6.67 1/°F	0.29

CF3 Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	485 MPa	205 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	70 ksi	30 ksi	6.67 1/°F	0.29

CF3M Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	485 MPa	205 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	70 ksi	30 ksi	6.67 1/°F	0.29

CF3MN Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	515 MPa	255 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	75 ksi	37 ksi	6.67 1/°F	0.29

CF8 Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	485 MPa	205 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	70 ksi	30 ksi	6.67 1/°F	0.29

CF8C Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	485 MPa	205 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	70 ksi	30 ksi	6.67 1/°F	0.29

CF8M Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	485 MPa	205 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	70 ksi	30 ksi	6.67 1/°F	0.29

CH10 Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	485 MPa	205 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	70 ksi	30 ksi	6.67 1/°F	0.29

CF16F Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	485 MPa	205 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	70 ksi	30 ksi	6.67 1/°F	0.29

CH20 Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	485 MPa	205 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	70 ksi	30 ksi	6.67 1/°F	0.29

CK20 Material Properties

Unit System	Young's Modulus, E	Density, ρ	Ultimate Strength, F_u	Yield Strength, F_y	Thermal Expansion Coef., α	Poisson's Ratio, ν
Metric	200,000 MPa	7,800 kg/m³	450 MPa	195 MPa	12 1/°C	0.29
Imperial	29,000 ksi	487 lb/ft³	65 ksi	28 ksi	6.67 1/°F	0.29