ASTM A513 Steel Properties
The below table outlines the material properties for ASTM A513 material including the young's modulus, yield strength, ultimate strength and other relevant mechanical properties required for structural and mechanical design.
ASTM A513 Young's Modulus
The Young's Modulus of ASTM A513 is 29,000 ksi.
ASTM A513 Ultimate Strength
The Ultimate Strength of ASTM A513 ranges between 38 and 110 ksi.
ASTM A513 Yield Strength
The Yield Strength of ASTM A513 ranges between 23 and 100 ksi depending on the material grade. See the below tables to get your specific material grade material strength.
As-welded Tubing Steel Properties
1008 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 290 MPa | 205 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 42 ksi | 30 ksi | 6.67 1/°F | 0.29 |
1009 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 290 MPa | 205 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 42 ksi | 30 ksi | 6.67 1/°F | 0.29 |
1010 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 310 MPa | 220 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 45 ksi | 32 ksi | 6.67 1/°F | 0.29 |
1015 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 330 MPa | 240 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 48 ksi | 35 ksi | 6.67 1/°F | 0.29 |
1020 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 360 MPa | 260 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 52 ksi | 38 ksi | 6.67 1/°F | 0.29 |
1021 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 370 MPa | 275 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 54 ksi | 40 ksi | 6.67 1/°F | 0.29 |
1025 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 385 MPa | 275 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 56 ksi | 40 ksi | 6.67 1/°F | 0.29 |
1026 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 425 MPa | 310 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 62 ksi | 45 ksi | 6.67 1/°F | 0.29 |
1030 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 425 MPa | 310 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 62 ksi | 45 ksi | 6.67 1/°F | 0.29 |
1035 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 455 MPa | 345 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 66 ksi | 50 ksi | 6.67 1/°F | 0.29 |
1040 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 645 MPa | 345 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 66 ksi | 50 ksi | 6.67 1/°F | 0.29 |
1340 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 495 MPa | 380 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 72 ksi | 55 ksi | 6.67 1/°F | 0.29 |
1524 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 455 MPa | 345 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 66 ksi | 50 ksi | 6.67 1/°F | 0.29 |
4130 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 495 MPa | 380 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 72 ksi | 55 ksi | 6.67 1/°F | 0.29 |
4140 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 620 MPa | 485 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 90 ksi | 70 ksi | 6.67 1/°F | 0.29 |
Normalized Tubing Steel Properties
1008 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 260 MPa | 160 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 38 ksi | 23 ksi | 6.67 1/°F | 0.29 |
1009 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 260 MPa | 160 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 38 ksi | 23 ksi | 6.67 1/°F | 0.29 |
1010 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 275 MPa | 170 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 40 ksi | 25 ksi | 6.67 1/°F | 0.29 |
1015 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 310 MPa | 205 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 45 ksi | 30 ksi | 6.67 1/°F | 0.29 |
1020 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 345 MPa | 240 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 50 ksi | 35 ksi | 6.67 1/°F | 0.29 |
1021 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 345 MPa | 240 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 50 ksi | 35 ksi | 6.67 1/°F | 0.29 |
1025 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 379 MPa | 255 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 55 ksi | 37 ksi | 6.67 1/°F | 0.29 |
1026 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 414 MPa | 275 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 60 ksi | 40 ksi | 6.67 1/°F | 0.29 |
1030 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 415 MPa | 275 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 60 ksi | 40 ksi | 6.67 1/°F | 0.29 |
1035 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 450 MPa | 310 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 65 ksi | 45 ksi | 6.67 1/°F | 0.29 |
1040 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 450 MPa | 310 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 65 ksi | 45 ksi | 6.67 1/°F | 0.29 |
1340 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 480 MPa | 345 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 70 ksi | 50 ksi | 6.67 1/°F | 0.29 |
1524 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 450 MPa | 310 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 65 ksi | 45 ksi | 6.67 1/°F | 0.29 |
4130 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 480 MPa | 345 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 70 ksi | 50 ksi | 6.67 1/°F | 0.29 |
4140 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 620 MPa | 450 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 90 ksi | 65 ksi | 6.67 1/°F | 0.29 |
Sink-Drawn Tubing Steel Properties
1008 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 330 MPa | 260 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 48 ksi | 38 ksi | 6.67 1/°F | 0.29 |
1009 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 330 MPa | 260 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 48 ksi | 38 ksi | 6.67 1/°F | 0.29 |
1010 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 345 MPa | 275 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 50 ksi | 40 ksi | 6.67 1/°F | 0.29 |
1015 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 380 MPa | 310 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 55 ksi | 45 ksi | 6.67 1/°F | 0.29 |
1020 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 415 MPa | 345 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 60 ksi | 50 ksi | 6.67 1/°F | 0.29 |
1021 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 425 MPa | 360 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 62 ksi | 52 ksi | 6.67 1/°F | 0.29 |
1025 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 450 MPa | 380 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 65 ksi | 55 ksi | 6.67 1/°F | 0.29 |
1026 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 480 MPa | 380 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 70 ksi | 55 ksi | 6.67 1/°F | 0.29 |
1030 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 480 MPa | 425 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 70 ksi | 62 ksi | 6.67 1/°F | 0.29 |
1035 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 550 MPa | 480 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 80 ksi | 70 ksi | 6.67 1/°F | 0.29 |
DOM Tubing Steel Properties
1008 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 415 MPa | 345 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 60 ksi | 50 ksi | 6.67 1/°F | 0.29 |
1009 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 415 MPa | 345 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 60 ksi | 50 ksi | 6.67 1/°F | 0.29 |
1010 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 415 MPa | 345 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 60 ksi | 50 ksi | 6.67 1/°F | 0.29 |
1015 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 450 MPa | 380 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 65 ksi | 55 ksi | 6.67 1/°F | 0.29 |
1020 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 480 MPa | 415 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 70 ksi | 60 ksi | 6.67 1/°F | 0.29 |
1021 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 495 MPa | 425 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 72 ksi | 62 ksi | 6.67 1/°F | 0.29 |
1025 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 515 MPa | 450 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 75 ksi | 65 ksi | 6.67 1/°F | 0.29 |
1026 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 550 MPa | 480 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 80 ksi | 70 ksi | 6.67 1/°F | 0.29 |
1030 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 585 MPa | 515 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 85 ksi | 75 ksi | 6.67 1/°F | 0.29 |
1035 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 620 MPa | 550 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 90 ksi | 80 ksi | 6.67 1/°F | 0.29 |
1040 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 620 MPa | 550 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 90 ksi | 80 ksi | 6.67 1/°F | 0.29 |
1340 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 655 MPa | 585 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 95 ksi | 85 ksi | 6.67 1/°F | 0.29 |
1524 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 620 MPa | 550 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 90 ksi | 80 ksi | 6.67 1/°F | 0.29 |
4130 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 655 MPa | 585 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 95 ksi | 85 ksi | 6.67 1/°F | 0.29 |
4140 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 760 MPa | 690 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 110 ksi | 100 ksi | 6.67 1/°F | 0.29 |
DOM Stress-Relieved Tubing Steel Properties
1008 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 380 MPa | 310 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 55 ksi | 45 ksi | 6.67 1/°F | 0.29 |
1009 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 380 MPa | 310 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 55 ksi | 45 ksi | 6.67 1/°F | 0.29 |
1010 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 380 MPa | 310 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 55 ksi | 45 ksi | 6.67 1/°F | 0.29 |
1015 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 415 MPa | 345 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 60 ksi | 50 ksi | 6.67 1/°F | 0.29 |
1020 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 450 MPa | 380 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 65 ksi | 55 ksi | 6.67 1/°F | 0.29 |
1021 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 470 MPa | 400 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 68 ksi | 58 ksi | 6.67 1/°F | 0.29 |
1025 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 480 MPa | 415 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 70 ksi | 60 ksi | 6.67 1/°F | 0.29 |
1026 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 515 MPa | 450 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 75 ksi | 65 ksi | 6.67 1/°F | 0.29 |
1030 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 550 MPa | 480 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 80 ksi | 70 ksi | 6.67 1/°F | 0.29 |
1035 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 585 MPa | 515 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 85 ksi | 75 ksi | 6.67 1/°F | 0.29 |
1040 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 585 MPa | 515 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 85 ksi | 75 ksi | 6.67 1/°F | 0.29 |
1340 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 620 MPa | 550 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 90 ksi | 80 ksi | 6.67 1/°F | 0.29 |
1524 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 585 MPa | 515 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 85 ksi | 75 ksi | 6.67 1/°F | 0.29 |
4130 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 620 MPa | 550 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 90 ksi | 80 ksi | 6.67 1/°F | 0.29 |
4140 Material Properties
| Unit System | Young's Modulus, E | Density, ρ | Ultimate Strength, Fu | Yield Strength, Fy | Thermal Expansion Coef., α | Poisson's Ratio, ν |
| Metric | 200,000 MPa | 7,800 kg/m3 | 725 MPa | 655 MPa | 12 1/°C | 0.29 |
| Imperial | 29,000 ksi | 484 lb/ft3 | 105 ksi | 95 ksi | 6.67 1/°F | 0.29 |